Urea formaldehyde molding compound A1 series
Melamine formaldehyde molding compound
urea-formaldehyde-triamine composite granule
The most high-end environmental protection type adhesives
 
 
Tel of international trade department:
+86 537 2316209 (86)15853706398
Fax: +86 537 3769999 2316209
WEBSITE:www.gaoximgmy.com
E-MAIL: jngx999@nokkonwud.com jngx888@nokkonwud.com
Address:Development Zone , jining city, shandong province, Chin
Product Your current location:HOME >> Urea formaldehyde molding compound A1 series
Urea formaldehyde molding compound A1

Name: urea formaldehyde resin molding compound is also called as urea molding compound. It is produced by adding curing agent, filling, colorant and lubricant into the urea formaldehyde resin.
Urea formaldehyde molding compound is widely used in producing the following products:

  1. Imitation Ceramic tableware, such as plates, bowl, chopsticks and so on;
  2. Entertainment products, such as mahjong,domino and so on;
  3. Daily necessities, industrial electric appliance housing, low-voltage electrical plug-ins and so on.

It has the following features: high strength, anti-scratch, anti-PH, anti-heat, no poison, good shining, bright color and no color changing issue with long term use.

Technical Specification: to GB13454-92 Standard


No.

Index

Unit

Type

Testing Method

A-

1

Appearance

 

After molding, the surface should be flat, shinny and smooth, no bubbles or crack, color and foreign material achieves standard.

 

2

Resistance to boiling water

 

No mushy, permit little color fade and purse

GB13454

3

Volatile matter

%,≤

4.00

GB13455

4

Water absorb (cold)

mg, ≤

100

GB1034

5

Shrinkage

%

0.60-1.00

GB13454

6

Distortion Temperature

℃≥

115

GB1634

7

Fluidity

mm

140-200

GB13454

8

Impact Strength (notch)

KJ/m2, ≥

1.8

GB1043

9

Bending Strength

Mpa, ≥

80

GB9341

10

Insulation Resistance after 24h in water

MΩ≥

104

GB1410

11

Dielectric strength

MV/m,≥

9.0

GB1408

12

Baking Resistance

GRADE

I

GB2407

Molding condition: (Reference only)


Temperature

150-180℃

Pressure

25-40Mpa

Curing time

0.24-0.3 min/mm

Package: Plastic knitting bag with inner one layer thin film bags, 25kg/bag.
Storage: Kept in airy, dry and cool room.
Storage period: Six months from production date. Test should be undertaken when expires. Qualified products can still be used.
Transportation Caution: Avoid moisture, heat, dirt and packaging damage.

 
HOME                          |                           ABOUT US                           |                           OUR PRODUCT                          |                          CONTACT US
Copyright @ 2010 All Rights Reserved Jining Gaoxing Timber Products Co., Ltd
TEL: 0537-3863158 3864618 3761111 FAX: 0537-3769999 Address:station of street office, wangyin town, national high tech Industrial Development Zone , jining city, shandong province, China
Alibaba : http://yzgxmy.1688.com/ (Trust Pass) http://gaoxingwood.en.alibaba.com/ (Export Pass)
ICP14009404